PA66 JA2700

Nkọwa Dị Mkpirikpi:

JA2700 bụ resin naịlọn 66 maka ebumnuche zuru oke. Resin a na-enye njikọta nke njirimara injinia nke ejiri ya mara.
ike dị elu; ike dị mma; mmetụta dị elu; ezigbo mmanụ ọkụ n'elu; iguzogide abrasion; obere okpomọkụ na-eguzogide;
iwepụ onwe onye.

Ọnụahịa: USD/MT nwere ike ịdị na nkwekọrịta

Port: SHANGHAI, NINGBO
MOQ: 1Mt
Nọmba ekwentị: 32131-17-2
Koodu HS: 3908101101
Ịkwụ Ụgwọ: TT, LC


Nkọwa Ngwaahịa

atụmatụ

Agba okike, Ọkara viscosity, Ebumnuche izugbe

Ngwa

Ọ dị mma maka ịkpụzi ihe na ịgba ntụtụ, a na-ejikwa ya eme ihe n'ọtụtụ ebe na monofilament na staple.ngwa kachasị na igwe, eletrọniki, eletriki, ngwa ọrụ, ihe ndị dị na ụgbọala, ụgbọ okporo ígwè, ngwa ụlọ,nkwukọrịta, ákwà, mmanụ ọkpọkọ/tankị na ngwaahịa injinia ziri ezi, wdg, enwere ike iji ya maka mmepụta ihe nkiri,Nkwakọ ngwaahịa, ngwa ahụike, ihe egwuregwu, na ihe ndị dị mkpa kwa ụbọchị na ihe ndị ọzọ.

 

Nkwakọ ngwaahịa

Na 25kg/akpa, 26MT/40HQ nwere pallets

Akụ na ụba Usoro Ule Ọnọdụ Ule Ngalaba Nsonaazụ Ule
Ọkwa
JA2700
Ọkọlọtọ
Q/JHS J 002-2022
Njirimara Ndị Dị Mkpa
Viscositiki dị n'etiti / 96%H2SO4; Ihe achọrọ: 2.67±0.03 - 2.70
Ọdịnaya Mmiri Usoro Karl Fischer Ihe achọrọ: ≤0.5 % 0.31
Njirimara Mekaniki
Ike ọdụdọ GB/T 1040.1-2018 20mm/min MPa 73.0
Ogologo oge na ezumike GB/T 1040.1-2018 20mm/min % 64.0
Modulu tensile GB/T 1040.1-2018 20mm/min MPa 1237
Ike ịgbagọ GB/T 9341-2008 5mm/min MPa 98.00
Modulu na-agbagọ agbagọ GB/T 9341-2008 5mm/min MPa 2432.00
Ike Mmetụta Akpụkpụ Usoro GB/T 1843-2008 A 2.75J / 23℃, iru mmiri 50% kJ/m² 7.31
Njirimara nke okpomọkụ
Okpomọkụ Mgbagwo Okpomọkụ GB/T 1634.1-2019, GB/T 1634.2-2019 1.82MPa 75.5
Ndekọ Agbaze GB/T 3682.1-2018 230℃, 2160g, 10s g/nkeji iri 82.80
Njirimara Ndị Ọzọ
Ike nke Osimiri GB/T 2411-2008 HD - 80.0

 

Rịba ama:
Enwere ike iji PA66 mee ihe maka monofilament siri ike, ahịrị ịkụ azụ na njikọta. A na-atụ data dị n'elu site na ụlọ nyocha ụlọ ọrụ ahụ ma ọ bụ naanị maka ihe nlele ahụ, nke anaghị anọchite anya uru nkọwapụta nke ngwaahịa ọ bụla.