A na-akpọ ibe Polyamide 6—nke a na-akpọkarị ibe Nylon 6—aha njikọ amide (–CO–NH–) dị na macromolecules ha. Nylon 6 chips na-adịkarị ka granules ọcha, nwere ebe ịgbaze nke 210–220°C na okpomọkụ nke ihe dị ka 300°C. Ha na-agbaze na phenol na acid sulfuric a kpụkọrọ akpụkọ, na-egosipụta ihe mkpuchi eletriki dị mma, ma nwee ezigbo iguzogide alkalis na nchara. Nylon bụ eriri sịntetik kachasị eguzogide abrasion.
Ịdị ọcha dị elu, Na-egbuke egbuke, Ike nrụgide dị elu
Ngwa
Ákwà e ji emegharị ákwà, eriri ụlọ ọrụ na eriri, ihe nkiri Co-Extrusion.
Nkwakọ ngwaahịa
Akpa Jumbo 800Kg, 28MT/40HQ
Akụ na ụba
Usoro Ule
Ọnọdụ Ule
Ngalaba
Nsonaazụ Ule
Ọkwa
LX 275 BRT
Viscositiki dị n'etiti
FZ/T 51004-2011
25℃, 96%H2SO4, m:v = 1:100
/
2.75±0.03
Ike ndọda kpọmkwem
/
/
g/cm³
1.12
Ike mmeputa
ASTM D638
50mm/min
Mpa
67.00
Njehie na Break
ASTM D638
50mm/min
%
239.57
modulus tensile
ASTM D638
1mm/min
Mpa
2405.52
Ike flexural
ASTM D790
2mm/min
Mpa
100.62
modulus flexural
ASTM D790
2mm/min
Mpa
3317.33
Ike mmetụta Izod notched
ASTM D256
23℃
J/m
48.98
Oke mmiri mmiri na-agbaze
ASTM D1238
235℃, 2.16kg
g/nkeji iri
17.89
Okpomọkụ nke mgbapụ n'okpuru ibu
ASTM D648
1.82MPa, 3.2mm
℃
44.10
Nkọwapụta:
Ọnụọgụ ndị dị n'elu bụ ụkpụrụ nkịtị maka usoro ngwaahịa kwekọrọ, nke enyere dị ka ntụaka maka ngwaahịa ndị ahịa na-ahọrọ, na ezigbo uru ndị ahụ dabere na COA nke ngwaahịa ahụ.