A na-akpọ ibe Polyamide 6—nke a na-akpọkarị ibe Nylon 6—aha njikọ amide (–CO–NH–) dị na macromolecules ha. Nylon 6 chips na-adịkarị ka granules ọcha, nwere ebe ịgbaze nke 210–220°C na okpomọkụ nke ihe dị ka 300°C. Ha na-agbaze na phenol na acid sulfuric a kpụkọrọ akpụkọ, na-egosipụta ihe mkpuchi eletriki dị mma, ma nwee ezigbo iguzogide alkalis na nchara. Nylon bụ eriri sịntetik kachasị eguzogide abrasion.
Ịdị ọcha dị elu, Na-egbuke egbuke, Ike nrụgide dị elu
Ngwa
Ákwà e ji emegharị ákwà, eriri ụlọ ọrụ na eriri, ihe nkiri Co-Extrusion.
Nkwakọ ngwaahịa
Akpa Jumbo 800Kg, 28MT/40HQ
Akụ na ụba
Usoro Ule
Ọnọdụ Ule
Ngalaba
Nsonaazụ Ule
Ọkwa
LX340
Viscositiki dị n'etiti
/
25℃, 96%H2SO4, m:v = 1:100
/
3.40±0.03
Ike nrụgide
ASTM D638
50mm/min
Mpa
72.37
Njehie na Break
ASTM D638
50mm/min
%
82.59
Ike flexural
ASTM D790
2mm/min
Mpa
94.89
modulus flexural
ASTM D790
2mm/min
Mpa
2187.19
Ike mmetụta
ASTM D256
23℃
kJ/m²
2.68
Oke mmiri mmiri na-agbaze
ASTM D1238
235℃, 2.16kg
g/nkeji iri
5.90
Nkọwapụta:
Ọnụọgụ ndị dị n'elu bụ ụkpụrụ nkịtị maka usoro ngwaahịa kwekọrọ, nke enyere dị ka ntụaka maka ngwaahịa ndị ahịa na-ahọrọ, na ezigbo uru ndị ahụ dabere na COA nke ngwaahịa ahụ.