A na-akpọ ibe Polyamide 6—nke a na-akpọkarị ibe Nylon 6—aha njikọ amide (–CO–NH–) dị na macromolecules ha. Nylon 6 chips na-adịkarị ka granules ọcha, nwere ebe ịgbaze nke 210–220°C na okpomọkụ nke ihe dị ka 300°C. Ha na-agbaze na phenol na acid sulfuric a kpụkọrọ akpụkọ, na-egosipụta ihe mkpuchi eletriki dị mma, ma nwee ezigbo iguzogide alkalis na nchara. Nylon bụ eriri sịntetik kachasị eguzogide abrasion.
Ịdị ọcha dị elu, Na-egbuke egbuke, Ike nrụgide dị elu
Ngwa
Ákwà e ji emegharị ákwà, eriri ụlọ ọrụ na eriri, ihe nkiri Co-Extrusion.
Nkwakọ ngwaahịa
Akpa Jumbo 800Kg, 28MT/40HQ
Akụ na ụba
Usoro Ule
Ọnọdụ Ule
Ngalaba
Nsonaazụ Ule
Nọmba Klas
LX245 NA-EME KA Ọ DỊ MMA
Ọbara dị n'etiti
FZ/T 51004-2011
25℃, 96%H2SO4
/
2.50±0.03
Oke mmiri mmiri na-agbaze
GB/T 3682.1-2018
235℃, 2.16kg
g/nkeji iri
32.8
Nrụgide na-agbawa agbawa
GB/T 1040.1-2022
50mm/min
MPa
67.45
Ogologo Mgbawa
GB/T 1040.1-2022
50mm/min
%
99.95
Ike flexural
GB/T 9341-2008
2mm/min
MPa
89.99
modulus flexural
GB/T 9341-2008
2mm/min
MPa
2014.10
Ike mmetụta Izod notched
GB/T 1843-2008
23℃/5.5J
kJ/m²
3.16
Mmiri dị n'ime ya
Q/1500LXJXA001-2023
/
%
0.038
Ebe agbaze
Q/1500LXJXA001-2023
Ọkụ ọkụ 10℃/min
℃
226.9
Njupụta
GB/T 1033.1-2008
/
g/cm³
1.165
Nkọwapụta:
Ọnụọgụ ndị dị n'elu bụ ụkpụrụ nkịtị maka usoro ngwaahịa kwekọrọ, nke enyere dị ka ntụaka maka ngwaahịa ndị ahịa na-ahọrọ, na ezigbo uru ndị ahụ dabere na COA nke ngwaahịa ahụ.