| Mba. | Njirimara resin | Uru a na-ahụkarị | Nkeji | Usoro ule |
| 1 | Nnukwu ike ndọda, 23 ℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Akpụkpọ anụ shrinkage, 23 ℃, 3.2mm, 23 ℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | Ọnụego mgbaze, 220 ℃, 10kg | 22 | g/10 nkeji | ASTM D1238 |
| 4 | Ike tensile na Mpụta, 23℃, 50mm/min, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Mgbatị nkwụsi ike na Mpụta, 23℃, 50mm/min, 3.2mm | 5 | %, (Nkeji) | ASTM D638 |
| 6 | Mgbatị nkwụsi ike na nkwụsịtụ, 23'℃, 50mm/min, 3.2mm | 10 | %, (Nkeji) | ASTM D638 |
| 7 | Modulus tensile, 23 ℃, 50mm/min, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Ike mgbanwe, 23℃, 15mm/min, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Modulus Flexural, 23℃, 15mm/min, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Izod Mmetụta Ike, Achọpụtara, 3.2mm, 23℃ | 220 | J/m | ASTM D256 |
| 11 | Izod Mmetụta Ike, Achọpụtara, 3.2mm, -30℃ | 90 | J/m | ASTM D256 |
| 12 | Izod Mmetụta Ike, Achọpụtara, 6.4mm, 23℃ | 220 | J/m | ASTM D256 |
| 13 | Izod Mmetụta Ike, Achọpụtara, 6.4mm,-30℃ | 90 | J/m | ASTM D256 |
| 14 | Rockwell Hardness, R-Scale | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, Achọghị ya | 85 | Celsius C | ASTM D648 |
| 16 | VICAT, 50N, 50℃ / h | 92 | Celsius C | ASTM D1525 |
| 17 | Ọnụ ego nke RTI | 95 | Celsius C | UL 746B |
| 18 | Mechanical RTI nwere mmetụta | 95 | Celsius C | UL 746B |
| 19 | Mechanical RTI enweghị mmetụta | 95 | Celsius C | UL 746B |
| 20 | Ọkụ ọkụ, 1.5mm | HB | / | UL 94 |
| 21 | Ọkụ ọkụ, 3.0mm | HB | / | UL 94 |