BD265MO bụ heterophasic copolymer dị oke mmetụta nke dabere na teknụzụ Borstar Nucleation (BNT). Ngwaahịa a na-egosipụta ike mmetụta dị mma ọbụlagodi na obere okpomọkụ na ezigbo ike nhazi na ike siri ike.
Ihe ndị e ji ọkwa a mepụta na-egosi ezigbo àgwà ndị na-eme ka ihe ghara ịdị mma ma na-agbanwe agbanwe n'ihe gbasara agba dị iche iche.
Nkwakọ ngwaahịa
Akpa ihe mkpuchi dị arọ, ibu dị arọ 25kg kwa akpa
Ngwa
Nlekọta ụmụaka, ihe ụmụaka ji egwuri egwu, igbe, igbe na pallet, ihe ndị a na-eji arụ ọrụ dị arọ, ngwá ụlọ, ngwa teknụzụ
Nkọwapụta Ngwaahịa
Mba.
Njirimara
Uru nkịtị
Usoro Nnwale
1
Njupụta
900-910kg/m³
ISO 1183
2
Ọkwa Mmiri Gbazee (230°C/2.16kg)
7g/nkeji iri
ISO 1133
3
Modulu ike ndọda (1mm/min)
1200MPa
ISO 527-2
4
Nrụgide nrụgide na mmepụta (50mm/min)
6%
ISO 527-2
5
Nrụgide nrụgide na mmepụta (50mm/min)
22MPa
ISO 527-2
6
Modulu Flexural
1250MPa
ISO 178
7
Ike Mmetụta Charpy, nke a na-akpọchi (23°C)
Enweghị ezumike
ISO 179/1eA
8
Ike Mmetụta Charpy, nke a na-akpọchighị akpọchi (-20°C)